COMPARAZIONE BARRIERE ALLUMINIO / EVOH ALU BARRIER BARRIERA ALLUMINIO THICKNESS 100 MICRON SPESSORE STEAM TRASMISS.RATE <0,5G/M2 24H (40 CELSIUS D. 90%RH) RATA VAPORE OXYGEN TRANSMISS.RATE <0,5ML3 (M2 24H 0,1MPA) RATA OSSIGENO PUNCTURE RESISTANCE >24 POUND EVOH BARRIER BARRIERA EVOH THICKNESS DART DROP ASTM D1709 TENSILE STRENGHT AT BREAK ASTM D882 ELONGATION AT BREAK 100 MICRON SPESSORE 200 G RES.PERFORAZIONE MD 20 Mpa RES.ROTTURA TD 19MPa MD 400 % ASTM D882 ELEMENDORF TEAR RESISTANCE RES.PERFORAZIONE PD 400 % MD 10 g/micron ASTM D1922 E-MODULUS ASTM D882 COEFFICIENT OF OUTER LAYERS FRICTION ASTM D1894 TD 2 g/micron RES. STRAPPO MD 330 Mpa MODULO TD 330 Mpa RES. ATTRITO >0,4 OXYGEN TRANSMISSION RATE RES.ALLUNGAMENTO RATA OSSIGENO ASTM D3985 <3,5 cm3 (m2 x day x bar) (23celsius degrees, 75% rh) SISAM AGENTI S.r.l. - Scali Cerere, 15 - 57122 LIVORNO - Tel: +39 0586 243818 - email : [email protected]