The Lineup of Electrolytic Copper Powder
For Carbon Brush
＃５２－Ｄ
Apparent Density
(g/cm3)
1.6～1.8
＃５２－H
Apparent Density
3
(g/cm )
1.5～1.7
＃５１－Ｎ
Apparent Density
3
(g/cm )
1.0～1.25
＃５１－Ｒ
Apparent Density
3
(g/cm )
1.0～1.15
Particle Size Distribution　(sieve analysis μm　-　%)
＋74
+63
+44
< 0.5
<1
1～8
-44
92～99
D50
(μm)
20～25
Particle Size Distribution　(sieve analysis μm　-　%)
＋74
+63
+44
< 0.5
<1
0.5～9
-44
90～99.5
D50
(μm)
20～25
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
< 0.5
<1
<3
5～20
-44
80～95
D50
(μm)
25～35
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
0
< 0.5
<1
0.5～7
-44
93～99.5
D50
(μm)
20～25
#51-N
#52-H
#51-R
For PM Bearings
＃３４（２０）
Apparent Density
3
(g/cm )
2.0～2.2
＃３５
Apparent Density
3
(g/cm )
2.35～2.5
＃Ｃ－ＳＰ
Apparent Density
(g/cm3)
1.9～2.3
+177
< 0.5
Particle Size Distribution　(sieve analysis μm　-　%)
+149
+105
＋74
+63
+44
<3
19～29
20～30
12～22
13～23
-44
14～24
D50
(μm)
70～90
+177
< 0.5
Particle Size Distribution　(sieve analysis μm　-　%)
+149
+105
＋74
+63
+44
<2
11～21
21～31
12～22
14～24
-44
17～27
D50
(μm)
70～90
+149
<1
Particle Size Distribution　(sieve analysis μm　-　%)
-63
+63
+105
25～65
20～65
5～25
#34(20)
#C-SP
D50
(μm)
70～90
For PM Friction Materials
＃５１－Ｎ
Apparent Density
3
(g/cm )
1.0～1.25
＃５１
Apparent Density
(g/cm3)
1.2～1.4
＃５１－Ｙ
Apparent Density
3
(g/cm )
1.4～1.6
＃Ｃ－ＳＰ
Apparent Density
(g/cm3)
1.9～2.3
＃１－６０
Apparent Density
3
(g/cm )
2.3～2.8
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
< 0.5
<1
<3
5～20
-44
80～95
D50
(μm)
25～35
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
< 0.5
<3
<　12
10～18
-44
75～84
D50
(μm)
25～35
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
0
<1
<　2
5～15
-44
85～95
D50
(μm)
25～35
Particle Size Distribution　(sieve analysis μm　-　%)
63
-63
+149
+105
25～65
20～65
<1
5～25
+250
2～15
+177
40～60
Particle Size Distribution　(sieve analysis μm　-　%)
+149
+105
＋74
+63
20～35
5～20
<5
<　2
#51-Y
#1-60
D50
(μm)
70～90
+44
<　2
-44
<　2
#C-SP
For PM Machine Parts
＃５２－Ｄ
Apparent Density
3
(g/cm )
1.6～1.8
＃ＦＳＰ
Apparent Density
3
(g/cm )
1.2～1.5
＃５２
Apparent Density
3
(g/cm )
1.9～2.3
＃1５２-NS
Apparent Density
3
(g/cm )
2.8～3.2
Particle Size Distribution　(sieve analysis μm　-　%)
＋74
+63
+44
< 0.5
<1
1～8
-44
92～99
D50
(μm)
20～25
Particle Size Distribution　(sieve analysis μm　-　%)
+63
+44
<3
5～17
-44
83～95
D50
(μm)
30～36
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
<0.5
<2
<5
10～20
-44
75～85
D50
(μm)
30～45
Particle Size Distribution　(sieve analysis μm　-　%)
+105
＋74
+63
+44
<0.5
<0.5
<1
5～15
-44
85～95
D50
(μm)
25～35
Contact: TEL+81-3-5573-6577
E-mail [email protected]
Copper Coated Powder for PM Bearings
1. Copper Coated Solid Lubricant Powder
Copper Coated Molybdenum disulfide　Powder : SC-350
Apparent Density Particle Size Distribution　(sieve analysis μm　-　%) Cu　Weight
3
（％）
+177
+149
+44
-44
(g/cm )
1.1～1.6
< 0.5
<5
35～65
40～65
47～53
Copper Coated Graphite Powder : PC-350
Apparent Density Particle Size Distribution　(sieve analysis μm　-　%) Cu　Weight
3
（％）
+177
+149
+44
-44
(g/cm )
0.6～1.0
< 0.5
<　7
45～75
25～50
47～53
SC-350
PC-350
2. Copper Coated Iron Powder
Copper Coated Iron Powder : FC-330
Particle Size Distribution (sieve analysis μm - %)
Apparent Density
3
+250
+177
+149
+44
-44
(g/cm )
1.65～1.85
0
< 0.5
< 5
65～85
15～30
Cu Weight
（％）
30～33
FC-330