CAB-O-SIL m-5f and eh-5f Fumed SILICA
for FOOD APPLICATIONS
APPLICATION GUIDE
®
System
Cab-O-Sil Food-Grade Fumed Silica Benefits
CARRIER, FLAVOR MASKING AGENT: CAB-O-SIL food-grade
fumed silica adsorbs liquids to produce dry powders that can
be easily mixed with other solids. At higher concentrations,
CAB-O-SIL fumed silica can act as a flavor masking agent to
facilitate the formulation of fortified/nutritious foods.
MICROENCAPSULATION: CAB-O-SIL food-grade fumed silica
encapsulates volatile compounds, reducing evaporation rates.
This increases flavors’ shelf life and reduces costly losses due
to flavor change in the final product.
LIQUIDS &
SEMI SOLIDS
DRYING AID, PROCESS EFFICIENCY: CAB-O-SIL food-grade
fumed silica reduces clogs in the spray dryer atomizer and
decreases the amount of product sticking to the walls; it
delivers higher powder recovery, improves drying efficiency,
and increases throughput by facilitating lower spray dryer
atomizer temperatures.
THICKENING, ANTI-SETTLING, EMULSIFICATION:
CAB-O-SIL food-grade fumed silica is an effective thickening,
emulsification, and anti-settling agent, due to its ability to
form a network and hold heavier ingredients in place. Its
low sensitivity to temperature and pH makes it an attractive
replacement for other stabilizers and viscosity control agents.
POWDERS
Application Examples
3 Vitamin E and
Omega 3 adsorption
3 Masking of bitter/
metallic flavors
3Flavor
microencapsulation
3 Non-dairy coffee
creamer
3 Spray dried
tomato powder
3 Canned vegetable
oil spray
3 Salad dressing
3 Frozen desserts
3 Gelling oils
3 Pickering emulsions
3 Automatic coffee
powder dispensing
CAB-O-SIL food-grade fumed silica acts as a spacer and moisture
adsorbent, reducing lump formation and crystallization, and
facilitating free flow, exact dosing, and storage stability.
3 Snacks’ powdered
flavors
end
product
Liquid adsorption
Anti-settling
Improved flow
Improved dispensability
Increased storage stability
Improved aesthetic appeal
Liquid thickening
•
•
•
•
•
•
•
Microencapsulation
Transparency
Conditioning agent
Increased drying rates
Flavor masking
Lipid substitution
Improved process efficiency
Adsorption
Microencapsulation
Dispersability
Anti-settling
Anti-caking
Transparency
Surface Area
CAB-O-SIL M-5F
Fumed Silica
CAB-O-SIL EH-5F
Fumed Silica
***
***
*****
***
***
***
200 m2/g
*****
*****
***
***
***
*****
380 m2/g
Performance: Best = ***** Good = ***
Health & Safety
•
•
•
•
•
High purity, food grade silica quality.
Colorless, odorless, tasteless.
No Genetically Modified Organisms.
Products do not contain common food allergens.
Food Grade Statement provided by Cabot Corp.
Regulatory Compliance
3Low calorie frozen foods
CAB-O-SIL M-5F and EH-5F fumed silica are silicon dioxides that:
• Are approved food additives (E551) per listing in EC
Regulation N° 1333/2008.
• Are labeled according to EC Regulation N° 1333/2008.
• Meet the purity criteria of E551 monograph as laid out in EU
Regulation 231/2012.
• Are determined as US FDA GRAS per scientific
procedure established under 21 CFR170.30 ( b )
3Pickering emulsions
for fat substitution
Cabot GmbH, Rheinfelden plant is a registered food ingredients
supplier and is HACCP, Kosher and Halal certified.
3 Powdered egg whites
LIPID SUBSTITUTION, TEXTURE, AESTHETIC APPEAL:
•
•
•
•
•
•
•
Selection Guide
FREE FLOW, TRANSPARENCY, STORAGE STABILITY:
CAB-O-SIL food-grade fumed silica facilitates the substitution
of up to 40% of fat contained in foods, by: a) providing a
more homogeneous lipid distribution to enhance the fat’s
effectiveness; and b) acting as an effective stabilizer of
Pickering emulsions that replace fat fractions. In both cases,
the organoleptic properties of the final product are preserved.
CAB-O-SIL Food-Grade Fumed Silica Benefits
3Extruded snacks
3Baked cookies
CAB-O-SIL® M-5F and eh-5f Fumed SILICA for FOOD APPLICATIONS
APPLICATION GUIDE
CARRIER
SPRAY DRYING AID
Liquid, semisolid, or pasty substances can be converted into
dry flowing powders by adding CAB-O-SIL M-5F fumed silica.
Improved carrier performance occurs at higher adsorption values.
CAB-O-SIL EH-5F fumed silica can improve spray-drying thermal
Increased CAB-O-SIL EH-5F fumed silica concentrations can lead
1000 clogs in the atomizer and deliver
efficiency M-5F
by up to 10%, prevent
to a substantial increase
CAB-O-SIL
1000 in viscosity. Mixing at low shear forces
830
820
CAB-O-SIL M-5F
820 fragment the
higherGel
powder recovery. It also can increase higher throughput,
achieves the best results, as830
high blending speeds
Silica
Silica Gel
M-5F formed by CAB-O-SIL fumed silica, reducing viscosity.
as spray dryers can be operated with a lower outlet temperature. CAB-O-SILnetwork
CAB-O-SIL M-5F
Silica Gel
Silica Gel
430
500
390
430
500
Spray Drying Thermal Efficiency
Thickening
of Soybean Oil 390
800
600
830
80%
820
430
390
400
Efficiency (%)
1000
CAB-O-SIL M-5F
Silica Gel
200
0
75%
20,000
Orange Oil
Lemon Oil
70%
65%
60%
Orange Oil
0
73
Lemon Oil
9% thermal efficiency increase
64
Viscosity (cps)
Oil Adsorption Values
(g/100g of Silica)
THICKENING
6 rpm
12 rpm
Orange
Oil
30 rpm
Lemon Oil
10,000
5,000
0
0.0%
0
15,000
0.2%
0.4%
0.6%
% CAB-O-SIL EH-5F fumed silica
0.5%
1.0%
1.5%
2.0%
2.5%
3.0%
% CAB-O-SIL EH-5F fumed silica (g/100 g oil)
FREE FLOW
LIPID SUBSTITUTION
FINAL PRODUCT STORAGE STABILITY
CAB-O-SIL M-5F fumed silica offers equivalent performance
as a flow aid when compared to precipitated silica, with the
advantage that it does not dull the natural food color (whereas
precipitated silica does). This is thanks to its low refractive index
of 1.46 and to the lower loading required.
CAB-O-SIL EH-5F fumed silica lowers moisture loss, reduces
lipid oxidation, and provides stabilization against staling, all
while reducing the required lipid fraction. Example: low-calorie
soft cookies.
CAB-O-SIL EH-5F fumed silica can improve the texture of
extruded foods, as measured by breaking strength, which
is a proxy for crispiness or brittleness.
Tomato powder
and precipitated silica*
Tomato powder
and fumed silica*
Hardness value of low-calorie cookies
70% Wheat Starch / 30% Gluten Extrudate Shear
Bubble Size = Force (g) à Hardness (lower is better)
Force (N) à Crispiness / Brittleness
% Oil
20%
15%
250
10%
410
5%
For illustration purposes only
*
NORTH AMERICA
Cabot Corporation Business
and Technical Center
157 Concord Road
Billerica, MA 01821 USA
cabotcorp.com
R01 10/13 ©2013 Cabot Corporation
Customer service:
Tel: +978 663 3455
Fax: 800 462 2313
Fax: +978 670 6167
1000
800
Lowering oil content makes cookie become harder
400
280
200
Adding CAB-O-SIL EH-5F
makes low-calorie cookie softer
0.0%
1.0%
2.0%
% CAB-O-SIL EH-5F fumed silica
SOUTH AMERICA
Cabot Brasil Industria
e Comericio Ltda.
Rua do Paraiso 148 - 5 andar
04103-000 Sao Paolo,
SP Brazil
Europe
Cabot Specialty Chemicals
Coordination Center
Interleuvenlaan 15 i
3001 Leuven
Belgium
Customer service:
Tel: +55 11 2144 6400
Fax: +55 11 3253 0051
Sales and Technical Support:
Tel: +32 16 39 24 00
Tel: +32 16 39 24 13
Fax: +32 16 39 24 44
[email protected]
Asia Pacific
Cabot China Ltd.
558 Shuangbai Road
Shanghai 201108
China
Tel: +86 21 6434 7766
Tel: +86 21 6434 1669
Fax: +86 21 6434 5532
Fax: +86 21 6434 1869
600
3.0%
0
No oil in mixture
0.0%
0.5%
1.0%
1.5%
2.0%
% CAB-O-SIL EH-5F fumed silica
CAB-O-SIL is a registered trademark of Cabot Corporation.
This information is provided as a convenience and is for informational purposes only. The data and conclusions
contained herein are based on work believed to be reliable; however, Cabot cannot and does not guarantee
that similar results and/or conclusions will be obtained by others. This information may contain inaccuracies,
errors or omissions. CABOT DISCLAIMS ALL WARRANTIES, EXPRESS AND IMPLIED, INCLUDING WARRANTIES FOR
MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE AS TO (i) SUCH INFORMATION, (ii) ANY PRODUCT AND
(iii) INTELLECTUAL PROPERTY INFRINGEMENT. In no event is Cabot responsible for, and Cabot does not accept
and hereby disclaims liability for, any damages in connection with the use of or reliance on this information or
any product to which it relates. Buyer assumes full responsibility for testing and determination of suitability of
a Cabot Product for Buyer’s intended application or use according to the applicable food requirements.
FUMED METAL OXIDES
CAB-O-SIL® MULTIFUNCTIONAL EXCIPIENT
FOR PHARMACEUTICALS
CAB-O-SIL FUMED SILICA IN SOLID DOSAGE FORMS
LIQUID AND SEMI-SOLID DOSAGE FORMS
TASTE MASKING AGENT
FREE FLOW
Improves flow for tableting and capsule
filling, leading to increased production
yields and tablet weight uniformity.
Can be used as part of a
microencapsulation system to mask
taste or protect sensitive ingredients
from degradation. Can be loaded
in the microcapsule wall to help
nucleate crystalline domains, or can
be loaded at the core/microcapsule
wall interface to increase stability or
alter the viscosity.
MOISTURE ADSORPTION
Due to its hydrophilic chemical
structure, can act as a scavenger of
moisture and help stabilize drugs that
require an acidic pH for optimal stability.
In granulation processes, can enable
uniform particle size distribution
via disintegration of large wet
agglomerates and redistribution of
the moisture in the mixture.
Can stabilize highly concentrated
pigment suspensions, preventing
them from settling in liquid tablet
coatings. Can be added to build-up
powders to improve flow and
promote fast drying.
CAPSULE ANTI-BLOCKING
Can increase throughput by reducing
clogs in the spray dryer atomizer and
decreasing the amount of product
sticking to the walls. Can improve the
drying profile of tacky materials or
act as a nucleation aid.
Can be added to the capsule shell wall
to form a smooth film. Can promote
high-speed filling of gelcaps by
reducing adhesion of the liquid filling
to the machinery.
CAB-O-SIL
fumed silica
Surface
Area
Tapped
Density
M-5P
200 m /
< 60 g/l
2 g
TABLET COATING
SPRAY DRYING AID
CONTROLLED DRUG RELEASE
TYPICAL PROPERTIES
Features
Easy to disperse
The data above are typical test values intended as guidance
only, and are not product specifications. Product specifications
are available from your Cabot representative.
APPLICATION OVERVIEW
Adjusting the concentration of fumed
silica can facilitate the control of drug
release rates. For poorly soluble drugs,
it can increase the dissolution rate.
This is achieved by dissolving the
drug in an organic solvent with the
fumed silica and evaporating the
mixture to dryness. Fumed silica can
also decrease dissolution rates in
controlled-release liquid dosage forms
by increasing viscosity.
STABILIZATION,
ANTI-SETTLING
Can enable the stabilization of
dispersions of solids in liquids and
prevent the formation of sediments
in liquid suspensions.
THICKENING
Can convert non-polar liquids
into spreadable gels. Promotes
gel stability at body temperature,
enabling applications where precise
area-dosing is required.
TRANSPARENCY
Clear gels can be formulated if the
refractive index of the product
matches that of CAB-O-SIL fumed
silica (1.46).
STABILITY AND
UNIFORM DISTRIBUTION
Can improve the consistency and
stability of a suppository. Can
increase the softening point without
affecting the melting point.
SPRAYING AID
In topical aerosol products can help
reduce clogs in the atomizer and
prevent the formation of sediments.
CAB-O-SIL® MULTIFUNCTIONAL EXCIPIENT FOR PHARMACEUTICALS
PERFORMANCE AS A GLIDANT
APPLICATION OVERVIEW
CAB-O-SIL FUMED SILICA
Glidants are designed to improve the flow
properties of powders and reduce friction and
static charge in high speed tablet and capsule
machines. Glidants also prevent bridging in the
hopper, and enable increased tablet hardness,
uniformity in tablet weight and content. These
features are key to ensure product regulatory
compliance, maintain high productivity, reduce
waste from tablet breakage and minimize
content variability.
Product
Product Characteristics
◆
Cabot’s easiest to process glidant. Due its lower density, this product is easier to disperse in both
solid and liquid formulations.
◆
Due to its higher purity, M-5P fumed silica is recommended over lower purity precipitated silicas.
M-5P
Regulatory Compliance:
CAB-O-SIL M-5P fumed silica is in compliance with:
◆ USP 37/NF 32 colloidal silicon dioxide monograph.
◆ EP 8th Ed. (2014) silica colloidal anhydrous monograph.
◆ JP 16th Ed (2011) light anhydrous silicic acid monograph.
PERFORMANCE REQUIREMENTS
Purity:
Higher
Untreated Fumed Silica
All CAB-O-SIL fumed silicas are produced through a pyrogenic process that results in one of the purest
commercially available forms of colloidal silicon dioxide as defined by the US Pharmacopeia. In contrast,
the production of precipitated silica requires the addition of a mineral acid to an alkaline silicate solution,
resulting in a lower purity product that contains higher moisture, sulfates and chloride impurities. These
impurities can have the following impact:
Low bulk
density
Purity
CAB-O-SIL M-5P
Fumed silica
◆
igh sulfates and chloride content can affect the stability of some active ingredients. Fumed silica has a
H
lower level of ionic sulfates and chloride than precipitated silica.
◆
igh levels of moisture can affect moisture-sensitive compounds. Fumed silica has a lower level of
H
moisture than precipitated silica.
Precipitated Silica
Lower
High bulk
density
Ease of Handling:
A powder’s “ease of use” is assessed according to its fluffiness, ease of handling, and storage. At higher bulk
densities and particle sizes the product is less fluffy and easier to handle and store.
Cabot Product
Competitive Product
More Difficult
Easier
Ease of Use / Dusting
The CAB-O-SIL name is a registered trademark of Cabot Corporation.
www.cabotcorp.com
R01 1/15 ©2015 Cabot Corporation
Technical Support
North America: 1 800 462 2313
South America: +55 11 2144 6400
Europe: +31 71 888 4132
Asia Pacific: +86 21 5175 8800
The data and conclusions contained herein are based on work believed to be reliable; however, Cabot cannot and does not guarantee that similar
results and/or conclusions will be obtained by others. This information is provided as a convenience and for informational purposes only. No guarantee
or warranty as to this information, or any product to which it relates, is given or implied. CABOT DISCLAIMS ALL WARRANTIES EXPRESS OR IMPLIED,
INCLUDING MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE AS TO (i) SUCH INFORMATION, (ii) ANY PRODUCT OR (iii) INTELLECTUAL PROPERTY
INFRINGEMENT. In no event is Cabot responsible for, and Cabot does not accept and hereby disclaims liability for, any damages whatsoever in
connection with the use of or reliance on this information or any product to which it relates.
FUMED METAL OXIDES
CAB-O-SIL® Fumed Silica
for Pharmaceutical and
Nutraceutical Applications
Cabot Corporation:
A Proud History of
Innovation and Quality
Cabot Corporation has been a global manufacturer of specialty chemicals
and performance products since 1882. We continue to innovate and find
applications for our materials in new fields, where they help improve
existing products and create exciting new offerings. Cabot is committed
to the reliable delivery of pharmaceutical materials of the highest quality
and consistency. Our global reach enables us to partner closely with our
ever-growing list of customers in order to become their supplier of choice
for quality materials, performance and service.
Current Challenges in Pharmaceutical and Nutraceutical Tablet Production
Producing tablets and capsules of uniform quality in an efficient manner can be challenging. The biggest issues tend to
occur during the following stages of the production process:
Flow through hopper
◆
Powders may stick to metallic walls
due to static charges that affect
flow patterns
◆
Agglomerates may form in the
hopper and this may result in
uneven flow as well as bridging
Die or capsule filling
The manufacture of tablets and
capsules on high speed machinery
requires the powder to exhibit optimal
flow. If optimal flow is not achieved,
the following issues can arise:
◆
Segregation of active or inactive
ingredients due to powder
cohesiveness
◆
Non-uniformity in tablet content
◆
Tablet weight variation
2
Tablet compaction
Variable tablet hardness caused by
poor powder compaction can lead
to capping, lamination, chipping, and
tablet breakage
CAB-O-SIL® FUMED SILICA FOR PHARMACEUTICAL AND NUTRACEUTICAL APPLICATIONS
CAB-O-SIL® Product Description
CAB-O-SIL M-5P (pharmaceutical grade) fumed silica is an excipient of extremely high purity used as a multi-functional
additive in the pharmaceutical and nutraceutical industries.
CAB-O-SIL fumed silica acts in the following ways to address significant issues involved in tablet production:
Flow aid
◆ CAB-O-SIL fumed silica’s glidant and
anti-static properties help improve the
flow properties of powders and reduce
friction and static charges in high
speed tablet and capsule machines.
Die filling aid
Compaction aid
◆ Uniformity in tablet weight and
◆ CAB-O-SIL fumed silica can aid in
active ingredient content result
from formulations that flow evenly
into the die cavity during the
tableting operation.
particle rearrangement within the die
during the early stages of compression
and can increase bonding strength
between powder particles that form a
solid tablet, helping to more effectively
compact tablets/capsules.
◆ Additionally, CAB-O-SIL fumed silica
helps prevent bridging.
◆ I ncreased tablet hardness at
lower compression forces results
from formulations that are
effectively compacted.
Physical-Chemical Properties
CAB-O-SIL fumed silica is compatible with many pharmaceutical ingredients. It adheres readily to hydrophilic ingredients,
functioning as an excellent glidant.
Pharmaceutical Product
Surface area
Bulk Density
Features
CAB-O-SIL M-5P fumed silica
200 m2/g
<60 g/l
Easy to disperse
The data above are typical test values intended as guidance only, and are not product specifications.
Product specifications are available from your Cabot representative.
Purity – CAB-O-SIL Fumed Silica versus Precipitated Silica
CAB-O-SIL fumed silica is produced through a pyrogenic process that results in one of the purest commercially available
forms of synthetic amorphous silica (99.8% pure). In contrast, the production of precipitated silica requires the addition of a
mineral acid to an alkaline silicate solution, resulting in a lower purity product that contains higher moisture, sulfates and
chloride impurities. These impurities can impact the product in significant ways, including:
◆
igh sulfates and chloride content can affect the stability of some active ingredients. Fumed silica has a lower level of
H
ionic sulfates and chloride than precipitated silica.
◆
igh levels of moisture can affect moisture-sensitive compounds. Fumed silica has a lower level of moisture than
H
precipitated silica.
3
CAB-O-SIL® FUMED SILICA FOR PHARMACEUTICAL AND NUTRACEUTICAL APPLICATIONS
Regulatory Compliance
CAB-O-SIL® fumed silica is produced in a manner consistent with Good Manufacturing Practices appropriate for
pharmaceutical excipients.
Pharmacopeia Status
Regulatory Agent
USP 37 / NF 32
EP 8th Ed. (2014)
JP 16th Ed. (2011)
CAB-O-SIL M-5P
fumed silica
Meets all requirements of
“Colloidal Silicon Dioxide”
Meets all requirements of
“Colloidal Anhydrous Silica”
Meets all requirements of
“Light Anhydrous Silicic Acid”
Performance
CAB-O-SIL Fumed Silica as Flow Aid
The formation of a powder bridge in a hopper of a tablet
press can lead to a phenomenon known in powder flow
as “bridging.” The image to the right illustrates
this phenomenon:
Powder Bridging in Hopper
How is flow measured?
The angle of repose provides a useful correlation to the
flow properties of powders. The relationship between the
angle of repose and powder flow is shown in Table 1
on the right.
Even Powder Flow in Hopper
TABLE 1: Correlation of Powder Flow to the Angle of Repose
Angle of Repose (degrees)
Flow
25 - 30
Very free flowing
30 - 38
Free flowing
38 - 45
Fair / passable flow
45 - 55
Cohesive
>55
Very cohesive
Source: Bodhmage, A. (2006). Correlation between physical properties and flowability
indicators for fine powders (Unpublished doctoral dissertation). University of
Saskatchewan, Saskatoon, Saskatchewan.
4
Figure 1 illustrates the flow properties of APAP
(acetaminophen or N-acetyl-p-aminophenol), ibuprofen
(isobutylphenylpropanoic acid) and aspirin (acetylsalicylic
acid) tablets when tested with various concentrations of
CAB-O-SIL® fumed silica. The results indicate that as the
concentration of CAB-O-SIL M-5P fumed silica increases,
the flowability of the powder mix improves, going from
‘cohesive’ to ‘passable flow’ to ‘free flowing’.
FIGURE 1: Effect of CAB-O-SIL M-5P fumed silica on APAP,
ibuprofen and aspirin flowability at various concentration levels
55
APAP
Ibuprofen
Aspirin
Angle of Repose
50
Cohesive
45
Fair /
passable flow
40
35
Free flowing
30
25
Very
free flowing
0
0.25
0.45
0.75
Concentration of CAB-O-SIL M-5P fumed silica (wt. %)
Figure 2 illustrates how the level of CAB-O-SIL M-5P
fumed silica in an APAP mixture influences the flowability
of the mixture. The results indicate that CAB-O-SIL M-5P
fumed silica improved flow properties of the APAP mixture,
taking it from a cohesive powder to fair/passable flow.
FIGURE 2: Effect of CAB-O-SIL M-5P fumed silica
on APAP mixture flowability
Angle of Repose (degrees)
55
55
Angle of Repose
50
APAP
Ibuprofen
Aspirin
45
40
Cohesive
50
45
Cohesive
40
Fair /
passable
flow
Fair / passable flow
35
Free
flowing
Free flowing
35
30
30
0
0.25
0.50
1.00
Concentration of CAB-O-SIL M-5P Fumed SIlica (wt. %)
Very free flowing
Figure 3 shows the different flow25rates of0 Avicel® PH-101
0.45
0.75
FIGURE 3: Effect of CAB-O-SIL M-5P fumed silica on Avicel™
Concentration
of CAB-O-SIL M-5P fumed
silica
wt.%
Micro Crystalline Cellulose (FMC Corporation)
when combined
PH-101 micro crystalline cellulose flow rate
with different loading levels of CAB-O-SIL M-5P fumed silica.
60
CAB-O-SIL M-5P Fumed Silica Loading (% wt.):
Note that without the addition of fumed silica, the powder
0.0
0.5
1.0
50
does not flow.
Flow Rate (ml/sec)
Angle of Repose (degrees)
40
CAB-O-SIL M-5P fumed silica
The data in Figure 3 was measured using the Hanson’s
55
FLODEX™ apparatus, which measures flow rates as a functionCAB-O-SIL M-5P
30fumed silica
CAB-O-SIL M-5DP fumed silica
Cohesive
of aperture diameter. The “bridging”
point
may
be
determined
50
20
with this apparatus by determining the aperture diameter
at which no flow of material will occur
into the lower
45
Cohesive
10
graduated cylinder.
Fair / passable
flow
No flow
0
40
35
16
18
20
Fair / passable flow
Aperature Diameter (mm)
Free flowing
22
Highly Hygroscopic Materials or Materials With Static Charge Problems
Free flowing
For highly hygroscopic materials30or materials that exhibit poor flow due to static charge, the amount of added CAB-O-SIL
0
0.25
0.50
1.00
M-5P fumed silica may need to be 3-4 times moreExcipient
than that
required
Addition
(wt. %)for materials that are less prone to static.
Very free flowing
5
CAB-O-SIL® FUMED SILICA FOR PHARMACEUTICAL AND NUTRACEUTICAL APPLICATIONS
CAB-O-SIL® Fumed Silica as a Die Filling Aid
Uniform tablet weights and uniform doses of active ingredients are dependent on the ability of the powder mix to feed into
the dies in a reproducible manner. Fumed silica can be added to the formulation in order to improve the flow properties of the
material and to aid particle rearrangement within the die during the early stages of die filling and compression.
Tablet Weight and Mixing Time
Formulations that flow evenly into the die cavity during the
tableting operation will result in uniform tablet weight and
drug content.
FIGURE 4: Effect of CAB-O-SIL M-5P fumed silica on tablet
weight at various concentrations & mixing times
410
1 minute
5 minutes
15 minutes
390
Avg. Tablet Weight (mg) / n=10
Figure 4 demonstrates that the weight of APAP tablets
can be influenced by the concentration of CAB-O-SIL M-5P
fumed silica in the formulation, as well as the time
of mixing.
370
350
330
310
290
270
250
0.1
0.25
0.5
Concentration of CAB-O-SIL M-5P Fumed Silica (wt. %)
Note: The formulation includes: 10% APAP and balanced lactose.
Bars correspond to minimum and maximum tablet weight.
Angle of Repose
Tablet Weight and Production Speeds
The addition of CAB-O-SIL M-5P fumed silica allows
tablet manufacturers to produce 55
high quality tablets at
higher tablet press speeds than they otherwise could,
50
therefore improving productivity.
FIGURE 5: Effect of CAB-O-SIL M-5P fumed silica &
press speed on tablet weight
APAP
Ibuprofen
Aspirin
Press Speed (rpm):
20
40
Cohesive
0.34
11% decline in average
tablet weight
45
Average Tablet Weight (g)
Figure 5 illustrates that at high production speeds, the
tablet weight of formulations that40do not include fumed
silica decreases by 11%, showcasing
issues with the
35
powder’s flow and die filling. In contrast, tablets that
30
include 0.25% CAB-O-SIL fumed silica
preserve a more
consistent weight under higher press
speeds.
25
60
Cohesive
0.33
Fair / passable flow
Fair /
passable flow
0.32
Free flowing
Free flowing
0.31
Very free flowing
Very
free flowing
0
0.45
0.75
0.3 silica wt.%
Concentration of CAB-O-SIL M-5P fumed
0.29
0.28
No Glidant
CAB-O-SIL M-5P
fumed silica
Note: Ibuprofen tablets with 0.25% CAB-O-SIL fumed silica.
6
Figure 6 illustrates that at high production speeds,
the addition of 0.25% CAB-O-SIL® M-5P fumed silica
reduced tablet weight variation anywhere from 30% to 40%
when compared to the same powder mix without a glidant.
FIGURE 6: Effect of CAB-O-SIL M-5P fumed silica
on ibuprofen tablet weight variation
Tablet Weight Relative Standard Deviation (%)
(Lower is better)
10.0
9.0
No Glidant
CAB-O-SIL M-5P fumed silica
30% lower tablet
weight variation
va
8.0
7.0
40
40% lower tablet
we
weight variation
6.0
5.0
4.0
3.0
2.0
1.0
0
40
60
Press Speed (rpm)
Note: Ibuprofen tablets with 0.25% CAB-O-SIL fumed silica.
API Content Uniformity
Addition of fumed silica reduces segregation of active
and inactive ingredients, promoting content uniformity.
FIGURE 7: Effect of CAB-O-SIL M-5P fumed silica on
coefficient of variation of API in tablet formulations
55
14
APAP
Cohesive
ohesive
0.5% CAB-O-SIL
M-5P fumed silica
Cohesive
No glidant
Coefficient of variation (%)
(Lower is better)
Angle of Repose
The data in Figure 7 demonstrates that the presence of
Ibuprofen
50
Aspirin
12
CAB-O-SIL M-5P fumed silica in a tablet formulation can
45 of active pharmaceutical
decrease the coefficient of variation
10
ingredient (API) content in a batch of tablets. Very low
40
variations in drug content were observed with APAP tablet
8
35
formulations containing 0.5% CAB-O-SIL
M-5P fumed silica
after blending for 15 minutes. Tablets without fumed silica
6
30
mixed for 15 minutes exhibited a coefficient of variation of
6%, which is 12 times higher than25the variation
seen in
4
0
0.45
0.75
tablets that did contain CAB-O-SIL fumedConcentration
silica.
of CAB-O-SIL M-5P fumed silica wt.%
Fair
flow
air / passable
p
Fair /
passable flow
Free flowing
of variation if glidant
Free flowing
12x higher coefficient
is not used
Very free flowing
Very
free flowing
2
0
1
5
Mixing Time (min)
15
Note: These tablets contained 10% APAP, 89.5% lactose and 0.5% CAB-O-SIL
M-5P fumed silica. The tablet formulation without fumed silica contained 90%
lactose and 10% APAP.
pose
55
50
APAP
Ibuprofen
Aspirin
45
7
Cohesive
Cohesive
Fair / passable flow
Fair /
passable flow
CAB-O-SIL® FUMED SILICA FOR PHARMACEUTICAL AND NUTRACEUTICAL APPLICATIONS
CAB-O-SIL® Fumed Silica as Compaction Aid
Tablet Hardness
CAB-O-SIL fumed silica was added to ibuprofen tablets in order to test its influence on tablet hardness. The results
of this testing under various compression force levels indicate the following conclusions and are illustrated in Figure 8 below:
◆
T he addition of only 0.25% of CAB-O-SIL fumed silica at 0.25mt of compression force facilitates an 81% improvement in
tablet hardness compared to tablets formulated without a glidant. Adding 0.25% CAB-O-SIL fumed silica increases tablet
hardness by 104% when compression forces reach 0.5mt.
◆
The addition of CAB-O-SIL fumed silica can double tablet hardness when compared to tablets formulated without a glidant.
Figure 8 indicates that the highest tablet hardness is
obtained at 1.5 metric ton of compression. This is relevant,
because as the compression forces are reduced, the
wear on press and dyes is reduced as well.
FIGURE 8: Effect of CAB-O-SIL fumed silica on tablet
hardness at various compression force levels
16
14
No Glidant
0.25% CAB-O-SIL M-5P fumed silica added
Tablet Hardness, Kcp
12
10
104%
improvement
in tablet
hardness
81% improvement
in tablet hardness
8
6
4
2
0
0.25
0.5
1.0
1.5
Compression Force, mt
SOUTH AMERICA
Cabot Brasil Industria e Comericio Ltda.
Rua do Paraiso
55 148 - 5 andar
04103-000 Sao Paolo,
SP Brazil
Tel: +55 11 50
2144 6400
Fax: +55 11 3253 0051
Angle of Repose
NORTH AMERICA
Cabot Corporation Business
and Technical Center
157 Concord Road
Billerica, MA 01821
USA
Tel: +978 663 3455
Fax: +978 663 5471
Tel: +678-297-1300 (Customer service)
45
EUROPE
SIA Cabot Latvia
101 Mukusalas Street
Riga, LV-1004,
APAP
Latvia
Ibuprofen
Tel: +371 6705 0984
Aspirin
Tel: +371 6705
0900
Fax: +371 6705 0985
40
MIDDLE EAST & AFRICA
Cabot Dubai
P.O. Box 17894
Cohesive
Jebel Ali Free Zone
LOB 15, Office 424
Dubai
United Arab Emirates
/ passable
Tel: Fair
+971-4-8871800
Fax: +971-4-8871801
ASIA PACIFIC
Cabot China Ltd.
558 Shuangbai Road
Cohesive
Shanghai 201108
China
Tel: +86 21 5175 8800
Fax: +86 21 6434 5532
flow
Fair /
passable flow
JAPAN
Cabot Specialty Chemicals Inc.
Sumitomo Shiba-Daimon Bldg. 3F
2-5-5 Shiba Daimon,
Minato-ku
Tokyo 105-0012
Japan
Tel: +81 3 6820 0255
Fax: +81 3 5425 4500
Free flowing
flowing
The CAB-O-SIL name is a registered trademark of Cabot Corporation. The AVICEL name is a registered trademark of FMC Corporation. The FLODEX name is a trademarkFree
of Hanson
Research Corporation.
The data and conclusions contained herein are based on work believed to be reliable; however, Cabot cannot and does not guarantee that similar results and/or conclusions will be obtained by others. This information is
35
provided as a convenience and for informational purposes only. No guarantee or warranty as to this information, or any product to which it relates, is given or implied. CABOT DISCLAIMS ALL WARRANTIES EXPRESS OR
IMPLIED, INCLUDING MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE AS TO (i) SUCH INFORMATION, (ii) ANY PRODUCT OR (iii) INTELLECTUAL PROPERTY INFRINGEMENT.
Very In no event is Cabot responsible for, and Cabot
Very free flowing
wing
does not accept and hereby disclaims liability for, any damages
30 whatsoever in connection with the use of or reliance on this information or any product to which it relates.
free fflowing
25
www.cabotcorp.com
0
0.45
0.75
Concentration of CAB-O-SIL M-5P fumed silica wt.%
©2015 Cabot Corporation.
ROI 1/15