International Journal of Scientific and Research Publications, Volume 4, Issue 7, July 2014
ISSN 2250-3153
1
Assessment of suitability of Fly Ash and Rice Husk Ash
burnt clay bricks
Akshay Satish More*, Ahad Tarade*, Ashwani Anant*
*
Department of Civil Engineering, KLS Gogte Institute of Technology, Belgaum.
Abstract- The proposed study involves the experimental
investigation of effect of fly ash and rice husk ash on the
properties of burnt clay bricks. Determination of properties of the
bricks casted with varying proportions of admixtures is taken up
to ascertain whether the admixtures can be used for the
production of clay bricks. On seeing the present day demand for
bricks, an attempt is made to study the behavior of bricks
manufactured using, different waste materials like rice husk ash
and fly ash The main aim of this research was to compare the
compressive strength of the bricks, so for this purpose different
percentage of materials were separately added 5%, 10%, 15%,
20% and 25% by weight and then the compressive strength of the
bricks was established, and then with the help of graph a
comparison between compressive strength of bricks, made out of
clay, Fly Ash, Rice husk ash and combination of all these was
determined. The bricks were made, sun dried and burnt in a kiln,
and then with the help of Compression Testing Machine
(C.T.M.) finely their compressive strength was calculated. From
this test in this research work it was concluded that the bricks
with fly ash as the waste material admixture, gave the highest
compressive strength. The fly ash admixture, in line with its
pozzolanic nature, was able to contribute in attaining denser
products with higher compressive strength, higher water
absorption rates, better durability and better overall performance.
The effects of the addition of rice husk ash and combination of
fly ash and rice husk ash by percentage-clay mix was also
investigated.
.
Index Terms- Bricks, Clay, Compressive strength, Fly Ash,
Rice Husk Ash, Water absorption.
I. INTRODUCTION
A
brick is a block made of clay burnt in a kiln. It is one of
the primary building materials known to mankind. Bricks
are composed of inorganic non-metallic material and are widely
used as building components all over the world. Over time,
bricks have appeared, gained prominence, lost importance and
then come to the forefront again with various styles of
architecture. Burnt bricks were used in ancient Indian, Babylon,
Egypt and Roman civilizations. Bricks find mention in the
Bible; the tower of Babel was built with burnt bricks.
The need for locally manufactured building materials
has been emphasized in many countries of the world because of
their easy availability and low cost. Bricks also have been
regarded as one of the longest lasting and strongest building
materials, made from locally available sources, used throughout
history. Ordinary building bricks are made of a mixture of clay,
which is subjected to various processes, differing according to
the nature of the material, the method of manufacture and the
character of the finished product. After being properly prepared
the clay is formed in molds to the desired shape, then dried and
burnt. Burnt bricks are usually stronger than sundried bricks,
especially if they are made of clay or clayey material. Burnt clay
bricks are weaker compared to bricks made of cement in terms of
strength and durability. Another important factor adding to the
disadvantages of burnt clay brick is the environmental impact
involved in the manufacturing process of clay bricks. To
overcome these drawbacks an attempt has been made to increase
the overall efficiency of clay brick by adding other suitable
materials along with clay in the manufacturing process. In this
project, we have tried to study the effects of adding fly ash and
rice husk ash to the conventional clay bricks. The effect of
addition of fly ash and rice husk ash, in varying percentages, to
different properties of clay bricks such as compressive strength,
water absorption etc. is investigated.
The construction industry in India contributes to about 10 % of
the Gross Domestic Progress (GDP), registering an annual
growth of about 9 %. Clay fired bricks form the backbone of the
construction industry which is valued at approximately US$ 70.8
billion. The brick sector in India, although unorganised, is
tremendous in size and spread. India is the second largest brick
producer (China dominates with 54 % share) in the world. It is
continuously expanding on account of a rapid increase in demand
for bricks in infrastructure and housing industries. In order to
meet this demand, over 150,000 brick units provide direct
employment to more than 8 million workers. During the eleventh
Five-year Plan period (2007-2012), the annual demand of 220
million bricks per year was estimated to be generating revenues
of over US$ 5.3 billion.
Considering all the points discussed above, there is a
need to find some alternative so as to reduce the impact of clay
brick manufacturing process on the environment and at the same
time increase the overall performance of the bricks. This research
aims to achieve both the mentioned improvements by using
admixtures along with clay during the manufacturing process.
Certain group of admixtures are added to increase the bond
between the particles and thus the strength of the brick. Such
admixtures are either cementitious or pozzolanic materials.
Pozzolanic materials include the traditional lime. The recent nontraditional pozzolanic admixtures used for brick production
include wood ash, sawdust ash and fly ash. A second category of
www.ijsrp.org
International Journal of Scientific and Research Publications, Volume 4, Issue 7, July 2014
ISSN 2250-3153
admixtures includes organic matter, such as rice husks, sawdust,
coal, etc., which burn out when the bricks undergo firing. They
regulate the temperature to which the brick is fired during
burning, which is of paramount importance. The higher the firing
temperature, the higher is the quality of the finished product. The
addition of admixtures serves the following purposes:
1.
2.
3.
4.
Addition of pozzolanic admixtures like fly ash, wood
ash etc. increases the strength of the brick.
As the organic admixture like saw dust, rice husk ash,
etc. burn out they leave pores in the product. This
permits the control of the bulk density of brick products
and help in producing lighter porous bricks. The pores
produced as the admixtures are burnt out permit the heat
to reach innermost part of the core, thereby avoiding unburnt cores.
The admixtures result in more uniformly burnt bricks,
especially when the firing is being done outside of
factory conditions, in which case inability to reach the
minimum desired temperature of 1000 °C results in unburnt cores especially in solid bricks.
Overall, there is a reduction in fuel and power
expenditures involved in the brick manufacturing
process.
II. MATERIAL USED FOR THE STUDY
2.1 CLAY:
Clay used for brick manufacturing should have the following
properties:



Plastic when mixed with water
Have enough tensile strength to keep its shape
Clay particles must fuse together
Clay soils are compounds of silica and alumina.
Calcareous clays have calcium carbonate and will burn to a
yellow or cream color. Non-calcareous typically contain feldspar
and iron oxides, and will burn to a brown, pink or red, depending
on the amount of iron oxide. The silica in the clay, when fired at
900-1200 degrees C, will turn to a glassy phase. This process,
called vitrification, will turn the clay to a crystalline structure.
Therefore, for the process of vitrification temperature is
important. If under-fired, the bonding between the clay particles
will be poor and the brick will be weak. If the temperature is too
high, the bricks will melt or slump. Vitrification does not have to
be complete, and does not actually occur in many of the small
traditional brickmaking plants around the world. However, the
vitrification does occur enough to give sufficient strength to the
brick. It takes approximately 3 cubic meters of clay soil to make
1000 bricks.
2
2.2 FLY ASH:
Fly ash is the by-product of coal combustion collected by the
mechanical or electrostatic precipitator (ESP) before the flue
gases reach the chimneys of thermal power stations in very large
volumes. All fly ash contain significant amounts of silicon
dioxide (SiO2), aluminum oxide (Al2O3), iron oxide (Fe2O3),
calcium oxide (CaO), and magnesium oxide (MgO). However,
the actual composition varies from plant to plant depending on
the coal burned and the type of burner employed. Fly ash also
contains trace elements such as mercury, arsenic, antimony,
chromium, selenium, lead, cadmium, nickel, and zinc.
These particles solidify as microscopic, glassy spheres
that are collected from the power plant‘s exhaust before they can
―fly‖ away — hence the product‘s name: Fly Ash. Chemically,
fly ash is a pozzolan. When mixed with lime (calcium
hydroxide), pozzolans combine to form cementitious compounds.
The power requirements of the country are rapidly
increasing due to growth of industries.65% of the total power
produced in India is by thermal power plants and hence there is
an increase in fly ash production. Further Indian coal contains 30
to 40% of ash content which further gives rise to air pollution,
soil pollution, disrupts ecological cycles and causes other
environmental hazards. Fly ash also contains traces of toxic
substances which may affect human health, plant life and also the
land on which fly ash is deposited. The disposal of this waste
material is a matter of great concern from the environmental and
ecological point of view. The safest and gainful utilization of fly
ash has been one of the topics of research over the last few
decades. The options of ash utilization including the ash based
products are at development stage and need to be made more
environments friendly by bringing ash revolution. It is estimated
at present nearly 160 million ton fly ash is produced every year.
2.3 RICE HUSK ASH:
Rice husk ash (RHA) is obtained by burning rice husk. Physical
properties of RHA are greatly affected by burning conditions.
When the combustion is incomplete, large amount of un-burnt
carbon is found in the ash. When combustion is completed, grey
to whitish ash is obtained.
The amorphous content depends on burning temperature
and holding time. Optimum properties can be obtained when rice
husks are burnt at 500 - 700°C and held for short time, this
temperature at which the husk is being burnt is less than that
required for formation of clinkers in cement manufacturing
process, the resulting ash can be used as a replacement of cement
in concrete. The Rice Husk ash used in plain cement concrete oft
en achieves economy and cost savings and imparts specific
engineering properties to finished products. The chemical
composition of RHA produced by utilizing the fluidized bed type
furnace is reported to be SiO2 (80-95%), K2O (1- 2%) and unburnt carbon (3-18%). The pozzolanic activity of rice husk ash is
effective in improving the strength.
www.ijsrp.org
International Journal of Scientific and Research Publications, Volume 4, Issue 7, July 2014
ISSN 2250-3153
3
III. MATERIAL TESTING
3.1SPECIFIC GRAITY:
The specific gravity test was done using pycnometer for all
samples passing through 4.75mm IS sieve.
TABLE NO. 3.1 SPECIFIC GRAVITY OF MATERIALS USED
Sl.No
1
2
3
Material
Clay
Fly Ash
Rice Husk Ash
Specific Gravity
2.25
2.00
0.45
IV. ANALYSIS AND RESULTS
Figure 4.1: Compressive strength of Fly ash bricks.
4.1 COMPRESSIVE STRENGTH TEST:
The compressive strength of the samples prepared was
determined in a Compression testing Machine. For the research 3
samples of each composition were tested and average of the
results is as tabulated below.
TABLE NO. 4.1COMPRESSIVE STRENGTH TEST RESULTS
Sl.
No.
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
Type of Sample
100% Clay
95% Clay + 5% Fly ash
90% Clay + 10% Fly ash
85% Clay + 15% Fly ash
80% Clay + 20% Fly ash
75% Clay + 25% Fly ash
95% Clay + 5% Rice Husk ash
90% Clay + 10% Rice Husk ash
85% Clay + 15% Rice Husk ash
80% Clay + 20% Rice Husk ash
75% Clay + 25% Rice Husk ash
95% Clay + 2.5% Fly ash + 2.5%
Rice Husk ash
90% Clay + 5% Fly ash + 5%
Rice Husk ash
85% Clay + 7.5% Fly ash + 7.5%
Rice Husk ash
80% Clay + 10% Fly ash + 10%
Rice Husk ash
85% Clay + 12.5% Fly ash +
12.5% Rice Husk ash
Avg compressive
strength (MPa)
4.938
5.074
5.126
5.457
5.801
6.081
5.027
4.806
4.288
3.991
3.823
3.786
Figure 4.2: Compressive strength of Rice Husk ash bricks.
5.039
5.199
5.509
5.753
Figure 4.3: Compressive strength of Fly ash and Rice Husk ash
bricks.
www.ijsrp.org
International Journal of Scientific and Research Publications, Volume 4, Issue 7, July 2014
ISSN 2250-3153
4
4.2 WATER ABSORPTION TEST:
The water absorption of the samples prepared was determined by
24 hour cold water immersion test. For the research 6 samples of
each composition were tested and average of the results is as
tabulated below.
TABLE NO. 4.2 WATER ABSORPTION TEST RESULTS
Sl.
No.
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
Type of Sample
100% Clay
95% Clay + 5% Fly ash
90% Clay + 10% Fly ash
85% Clay + 15% Fly ash
80% Clay + 20% Fly ash
75% Clay + 25% Fly ash
95% Clay + 5% Rice Husk ash
90% Clay + 10% Rice Husk ash
85% Clay + 15% Rice Husk ash
80% Clay + 20% Rice Husk ash
75% Clay + 25% Rice Husk ash
95% Clay + 2.5% Fly ash + 2.5%
Rice Husk ash
90% Clay + 5% Fly ash + 5%
Rice Husk ash
85% Clay + 7.5% Fly ash + 7.5%
Rice Husk ash
80% Clay + 10% Fly ash + 10%
Rice Husk ash
85% Clay + 12.5% Fly ash +
12.5% Rice Husk ash
Water Absorption
(%)
4.75
9.81
11.84
14.58
15.07
16.43
8.16
12.78
13.66
14.43
16.16
11.21
Figure 4.5: Water absorption of Rice Husk Ash bricks.
13.36
15.05
16.38
17.09
Figure 4.6: Water absorption of Fly Ash and Rice Husk Ash
bricks.
4.3. BLOCK DENSITY TEST:
The block density of the samples prepared was found out by
considering the dry weight and overall volume of 6 samples and
the average of the results is as tabulated below.
TABLE NO. 4.3: BLOCK DENSITY TEST RESULTS
Figure 4.4: Water absorption of Fly ash bricks.
Sl.
No.
Type of Sample
1
2
3
4
5
6
7
8
9
10
11
100% Clay
95% Clay + 5% Fly ash
90% Clay + 10% Fly ash
85% Clay + 15% Fly ash
80% Clay + 20% Fly ash
75% Clay + 25% Fly ash
95% Clay + 5% Rice Husk ash
90% Clay + 10% Rice Husk ash
85% Clay + 15% Rice Husk ash
80% Clay + 20% Rice Husk ash
75% Clay + 25% Rice Husk ash
Block Density
( Kg per cubic
meter)
1828.707
1825.580
1822.743
1771.367
1760.398
1734.171
1811.157
1799.099
1783.044
1767.668
1729.405
www.ijsrp.org
International Journal of Scientific and Research Publications, Volume 4, Issue 7, July 2014
ISSN 2250-3153
Sl.
No.
Type of Sample
12
95% Clay + 2.5% Fly ash + 2.5%
Rice Husk ash
90% Clay + 5% Fly ash + 5%
Rice Husk ash
85% Clay + 7.5% Fly ash + 7.5%
Rice Husk ash
80% Clay + 10% Fly ash + 10%
Rice Husk ash
85% Clay + 12.5% Fly ash +
12.5% Rice Husk ash
13
14
15
16
5
Block Density
( Kg per cubic
meter)
1814.726
1802.044
1789.672
1772.079
1735.154
Figure 4.9: Block Density of Fly ash and Rice Husk ash bricks.
V. CONCLUSIONS
Figure 4.7: Block Density of Fly ash bricks.
From the experimental results obtained, it can be concluded that
1. The clay burnt bricks manufactured with fly ash and
rice husk ash had similar appearance when compared to
the conventional clay bricks.
2. The clay bricks having fly ash as an admixture showed
the best performance, having a compressive strength of
about 23% greater than that of conventional bricks. The
percentage of water absorption for these bricks was
found to be more than that of conventional bricks but
still within the prescribed maximum limit as per Indian
Standards.(Maximum allowable water absorption as per
Indian Standards is 20%) Hence fly ash can be used as
an admixture with clay bricks.
3. The brick having rice husk ash as an admixture showed
lower compressive strength and higher percentage of
water absorption when compared to the conventional
clay bricks. Also, for higher percentages of rice husk
ash, the edges were found to be irregular in nature.
Hence, rice husk ash is not recommended to be used as
an admixture with clay bricks.
4. The bricks having both fly ash and rice husk ash as
admixtures in equal proportions showed a marginal
increase in strength for higher percentages of admixture.
The water absorption of these bricks was found to be
more than that of conventional bricks. Addition of both
the admixtures together gives only a small increase in
performance, hence it is not highly recommended
Figure 4.7: Block Density of Rice Husk ash bricks.
www.ijsrp.org
International Journal of Scientific and Research Publications, Volume 4, Issue 7, July 2014
ISSN 2250-3153
REFERENCES
[1]
[2]
[3]
[4]
[5]
[6]
[7]
Ashish Kumar Parashar and Rinku Parashar (2012), “Comparative Study of
Compressive Strength of Bricks Made With Various Materials to Clay
Bricks”, International Journal of Scientific and Research Publications,
Volume 2, Issue 7.
Agrawal B.N, Kohli S.M (2010), “New Building Materials and
Construction World”, Standard Publication House.
Samir Mistry (2002), “Thesis report on study on compressive strength of fly
ash bricks”, Sardar Patel University, V.V.Nagar, Gujrat.
Jayesh Pitroda (2010), paper on “A study of utilization aspect of fly ash in
Indian context”, presented at the National Conference on environmental
impact of thermal power plants .
IS 5454: 1978: Methods of sampling of Burnt Clay Bricks (First Revision)
IS 3495 (Parts 1 to 4): Methods of tests on Burnt Clay Bricks (Third
Revision)
American Association State Highway and Transportation Officials Standard
AASHTO No.: T 32-70 Designation: C 67 – 02c Standard Test Methods for
Sampling andTesting of bricks.
6
AUTHORS
First Author – Akshay Satish More, Final Year student in
Bachelor of Engineering in Civil Engineering, KLS Gogte
Institute of Technology, Udyambag, Belgaum.
Email: [email protected]
Second Author – Ahad Tarade, Final Year student in Bachelor
of Engineering in Civil Engineering, KLS Gogte Institute of
Technology, Udyambag, Belgaum.
Email: [email protected]
Third Author – Ashwani Anant, Final Year student in Bachelor
of Engineering in Civil Engineering, KLS Gogte Institute of
Technology, Udyambag, Belgaum.
Email: [email protected]
www.ijsrp.org