FARSOON FS121M
Accesible small frame metal
laser sintering system
FARSOON FS121M
SPECIFICATIONS
External Dimensions (LxWxH)
Weight
Effective Build Size (LxWxH)
Layer Thickness (Typical)
FS 121 M
1000 x 770 x 1700 mm
1000 kg
120 x 120 x 100 mm
Adjustable 0.02 - 0.08 mm
Volume Build Rate*
5 cm3/hr
Scanning Speed*
15.2 m/s
Scanner
Laser Type
Spot Diameter
Power Requirements
Powder Delivery
Powder Feed Mode
Inert gas supply
Fully digital dynamic-focusing, high-accuracy galvo scanning system
200W Yb-fibre laser
0.04 - 0.1 mm
3 kW Max
High performance heat resistant ceramic or silicon rubber blade
Uni-Directional powder feed system with single feed cylinder
Argon or Nitrogen
Gas protective system
Gas advection dust recovery system
Inert Gas Consumption
<3 L/min
Safety
Operating System
System Control Software
Data File Format
Material
Safety execution standard GB/T 15605-2008 dust explosive & pressure relief guide
Windows 7
Farsoon MakeStar-MTM open platform cotrol interface
.STL
FS 174 PH, FS 316 L, FS CoCr, FS Ti 64
* Build quality degradation may occur outside the effective build size. ** Max build rate, material dependent
Dental Crowns
Fuel Cell Cartridge Guide
Farsoon FS121M
Accesible small frame metal
laser sintering system
COMPACT
The FS121M is a increditly flexible system allowing the user to select between multiple
spot sizes and recoating blades, this combined with a small footprint and reduced
need for ancillary equipment allows the FS121M to match customer workspace, material
and application requirements.
HIGH TEMPERATURE
The FS121M features a 200W Yb-fiber laser and a fully digital scanning system.
These features along with a fine spot size allows for the creation of very detail and
complex parts. Farsoon is dedicated to high quality utilizing premium parts for all
key components and incorporates the latest safety systems with inert gas supply and
over-sized protective filter systems all at a price that is accessible for any business.
OPEN PLATFORM
Farsoon is the only laser sintering system producer offering fully open platforms, meaning
the user has previously-impossible levels of freedom and flexibility when it comes to
parameter adjustments for laser sintering production.
METAL LASER SINTERING MATERIALS
FS316L
FS17-4PH
FSCoCr
CoCr
Titanium Alloy
FSTi64
FSAlSi10Mg
Average Particle Size (D50)
30 ~ 40 μm
30 ~ 40 μm
25 ~ 40 μm
30 ~ 40 μm
25 - 35 μm
Particle Size Range (D10~D90)
20 ~ 60 μm
20 ~ 65 μm
15 ~ 65 μm
15 ~ 65 μm
20 ~ 60 μm
Apparent Density
3.5 ~ 4.5 g/cm3
4.0 ~ 4.5 g/cm3
4.0 ~ 5.0 g/cm3
2.0 ~ 2.5 g/cm3
1.33 g/cm3
Tap Density
4.5 ~ 5.5 g/cm3
4.5 ~ 5.5 g/cm3
5.0 ~ 6.5 g/cm3
2.5 ~ 3.0 g/cm3
1.68 g/cm3
Tensile Strength (Rm ) ASTM E8/E8M-13a
≥ 600 MPa
≥ 1050 MPa
≥ 1100 MPa
≥ 1050 MPa
430 ± 10 MPa
Yield Strength (Rp0.2 ) ASTM E8/E8M-13a
≥ 550 ± 50 MPa
950 ± 100 MPa
1000 ± 100 MPa
970 ± 100 MPa
276 ± 10 MPa
≥ 35%
≥ 15 %
≥ 5.0 %
≥ 8 %
3.0 ± 0.5%
Stainless Steel 316L Stainless Steel 17-4PH
Aluminium Alloy
General Properties
Mechanical Properties of Parts
Elongation after Fracture (A50mm ) ASTM E8/E8M-13a
©Farsoon/ LSS 2016 The information contained in this document is not contractually binding and may not be reproduced without prior approval.
Germany
China /Asia
America
LSS Laser Sinter Service GmbH
Farsoon Technologies
Varia 3D, Inc.
+49. 2301. 91 323. 0
+86. 7318. 39 761. 98
+1. 5128. 43 554. 5
[email protected]
[email protected]
[email protected]
www.lss-europe.com
www.farsoon.com
www.varia3d.com