Technical datasheet
Page 1 of 2
®
Sumitube O2
Dual Wall Polyolefin, 1:1
Operating Temperature: -55 up to 105°C
Surface: Glossy
Marking: None
ASTM D 2671
ISO 37
JASO M 104
JIS C 3005
Dimensions
BEFORE SHRINKAGE
DELIVERY UNITS *
AFTER SHRINKAGE
Inner diameter (EID) min.
Inner diameter (RID) max.
Wall thickness (RWT) min- max
Unit quantity
[mm]
[mm]
[mm]
[m]
[m]
6 x 0,7
6,00
4,50
nom. 1,20
200
1000
9 x 0,6
9,00
6,10
nom. 1,20
100
500
11 x 0,7
11,0
7,90
nom. 1,30
100
500
* Sizes 10,3mm, 13mm, 14mm and 17mm as well as drum of 2200 m are available upon request.
Colours & Technical drawing
STANDARD COLOURS
black
Box quantity
[type]
SPECIAL COLOURS
upon
request
TECHNICAL DRAWING
SUMITOMO- G-15032012 PM0809 ©2009 SUMITOMO ELECTRIC Schrumpf- Produkte GmbH. Subject to change. Tube colours may vary.
Technical datasheet
Page 2 of 2
®
Sumitube O2
Dual Wall Polyolefin, 1:1
Technical properties
PHYSICAL PROPERTIES
PROPERTY
TEST METHOD
REQUIREMENT
TYPICAL VALUE
Longitudinal Change
ASTM D 2671
Max. ± 5%
-1%
Specific Gravity
ASTM D 792
Max. 1,00
0,95
Tensile Strength
ISO 37
Min. 12 MPa
≥ 18 MPa
Elongation at Break
ISO 37
Min. 300%
≥ 460%
JIS C 3005
no cracking
Pass
(immersion IGEPAL 10%)
no growth
Pass
TEST METHOD
REQUIREMENT
TYPICAL VALUE
Operating Temperature
Life- Curve
-55 up to 105°C
-55 up to 105°C
Min. Shrink Temperature
Arrhenius- Plot
full recovery
115°C
Shrinking starts at
Arrhenius- Plot
Impact Test (-30°C)
Stress Cracking Test (50°C x 24h)
THERMAL PROPERTIES
PROPERTY
80°C
Elongation after heat ageing (120°C x 24h)
ISO 37
Min. 270%
≥ 500%
Tensile Strength after heat ageing (120°C x 24h)
ISO 37
Min. 12 MPa
≥ 14 MPa
Heat Shock (200°C x 4h)
ASTM D 2671
no crack, flowing or dripping
Pass
Brittle Point
ASTM D 746
Max. -55°C
-70°C
(under 2 bar x 5 min)
Min. 60%
≥ 75%
Deformation Resistance (140°C x 10 min)
CHEMICAL PROPERTIES
PROPERTY
TEST METHOD
REQUIREMENT
TYPICAL VALUE
Flammability
FMVSS 302
FMVSS 302
Pass
ISO 62
Max. 0,5%
Pass
Water Absorption
OTHER PROPERTIES
PROPERTY
TEST METHOD
REQUIREMENT
TYPICAL VALUE
(T- peel on ALU- pipe at 23°C)
Min. 10N/10mm
≥ 20N/10mm
Longitudinal Change *
ASTM D 2671
0 to -10%
-3%
Cold Impact (-40°C) *
DIN VDE 0472
no cracking
Pass
Cold Impact (-35°C x 4h) *
(-30°C x 0,5h)
no cracking
Pass
Adhesion Strength Test *
Salt Water Spray Test (3000h) *
NF- X 41.002
no corrosion
Pass
Heat Shock (200°C x 20min) *
ASTM D 2671
no crack, flowing or dripping
Pass
JASO M104
no rust
Pass
Chipping Resistance *
Fluid Resistance (after immersion 23°C x 72h) *
Bending Test (5 x on 25mm dia.) *
Stickiness (tightness) (after 120°C x 20 min) *
Impact Test *
Impact- Test
no cracking
Pass
(Visual check within 20 sec)
no cracking
Pass
(Visual checking)
Sticking on pipe, no peeling
Pass
(-30°C x 0,5h)
no cracking
Pass
* Tubing shrunk on metal pipe. Fluids: H2SO4. Nacl. Brake fluids SAE 1703 and LHM. High Octane Gasoline.
SUMITOMO- G-15032012 PM0809 ©2009 SUMITOMO ELECTRIC Schrumpf- Produkte GmbH. Subject to change. Tube colours may vary.