Technical Information
LUPOY PC 1303-10C
Polycarbonate Resin
Introduction
LUPOY PC 1303-10C resin is designed for extrusion and injection molding products. It exhibits an excellent
physical property balance of heat resistance, transparency and impact strength.
Main Characteristics
• UV stabilizer1
• Medium viscosity
• Appliances
• Outdoor appliances
Applications
Properties2
Physical
Melt Flow Rate (300 °C /1.2 kg)
Density
Mold Shrinkage
Water Absorption @ 24 hrs, 23°C
@ equilibrium, 50%RH, 23°C
Optical
Refractive Index, nD
Light Transmittance
Haze
Thermal
Deflection Temperature Under Load (DTUL) @ 4 mm
@ 66 psi (0.45 MPa), annealed
@ 264 psi (1.8 MPa), annealed
@ 264 psi (1.8 MPa), unannealed
Vicat Softening Point, 50°C /hr, 50N Load
Coefficient of Linear Thermal Expansion, @ -40 to 82°C
Mechanical
Tensile Yield Strength
Ultimate Tensile Strength
Elongation at Yield
Elongation at Break
Tensile Modulus
Flexural Strength
Flexural Modulus
Notched Izod Impact3 @ 23 °C
Unnotched Izod Impact @ 23 °C
Instrumented Dart Impact 4, Total Energy @ 23 °C
Rockwell Hardness
Taber Abrasion Resistance 5 (D Haze)
Ignition Resistance6
UL-94 @ 1.5 mm
UL-94 @ 3.0 mm
Limiting Oxygen Index
Ball Indentation Temperature
Average Extent of Burning
Electrical
GWT 2.0 mm, 5 second
Compression Tracking Index @ 2.0 mm
Dielectric Strength
Dielectric Constant @ 60 Hz
Dissipation Factor @ 60 Hz
Volume Resistivity @ 23 °C, dry
• Good mold release
• Automotive components
Test
Method
SI
English
Value
ASTM D 1238
ASTM D 792
ASTM D 955
ASTM D 570
ASTM D 570
10
1.20
0.005~0.007
0.15
0.32
ASTM D 542
ASTM D 1003
ASTM D 1003
Units
Units
in/in
%
%
10
1,200
0.005~0.007
0.15
0.32
g/10 min
kg/m3
mm/mm
%
%
1.586
89
0.7~1.5
%
%
1.586
89
0.7~1.5
%
%
ASTM D 1525
ASTM D 696
291
286
262
300
38 x 10-6
°F
°F
°F
°F
in/in/°F
144
141
128
149
68 x 10-6
°C
°C
°C
°C
mm/mm/°C
ASTM D 638
ASTM D 638
ASTM D 638
ASTM D 638
ASTM D 638
ASTM D 790
ASTM D 790
ASTM D 256
ASTM D 256
ASTM D 3763
ASTM D 785
ASTM D 1044
8,700
10,300
6
150
350,000
14,000
350,000
17
No break
770
118
45
psi
psi
%
%
psi
psi
psi
ft-lb/in
MPa
MPa
%
%
MPa
MPa
MPa
J/m
in-lb
R Scale
%
60
71
6
150
2,410
96
2,410
900
No break
87
73
45
ASTM D635
ASTM D635
ASTM D 2863
IEC 598-1
ASTM D 635
HB
HB
26
>125
1
%
°C
in
HB
HB
26
>125
25
IEC 695-2-1
IEC 112
ASTM D 149
ASTM D 150
ASTM D 150
ASTM D 257
850
250
420
3
0.001
2.0 x 10 17
ASTM D 648
g/10 min
Value
°C
V
V/mil
W-cm
850
250
17
3
0.001
2.0 x 10 17
J
M Scale
%
%
°C
mm
°C
V
KV/mm
W-cm
1. The addition of an UV stabilizer to a resin does not completely eliminate the effects of UV exposure but to slow down the rate at which the effects occur. These effects may include color shift,
decreased mechanical properties, and/or optical properties. Actual results may very depending on application and other factors such as resin color, transparency and additives. Therefore, actual
end-use testing is recommended.
2. Typical properties; not to be constructed as specifications.
3. 0.125 in; 10 mil notch (3.2 mm; 0.25 mm notch).
4. 0.125 in; 8000 ipm (3.2 mm; 203 m/min).
5. 1,000 g; CS-10 F wheel; 500 cycles.
6. These numerical flame spread ratings are small-scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions. UL 94 file: E67171.