PRODUCT INTRODUCTION SHEET
KK233 ENHANCED INTERFACE EMULSION (PRIMER)
DESCRIPTION
KINGKOTE KK233 ENHANCED INTERFACE EMULSION is formulated by using
acrylic resin polymer. It has excellent penetration and adhesion. KK233 is a multi-purpose
product. It can be used as primer, water-based paint additive, cement mixture, adhesive and
many more.
CHARACTERISTICS






KK233 is designed as primer to enhance the interface of the application area.
KK233 can be diluted by water in vary ratio for different purpose accordingly.
The diluted KK233 can be mixed with water-based paint to strengthen its colour durability
and extend the lifespan of paint.
Also, the diluted KK233 can be mixed with cement to enhance its interface and adhesion;
reduce water vapour transmission.
KK233 is odourless and water cleanable. It is an environmental friendly product.
Excellent bonding in wooden; concrete materials.
RECOMMENDED USES



Concrete: Balcony, RC Slab, RC Roofing, RC Gutter, Swimming Pool and etc.
Metal: Metal Roofing, Water Tank, Metal Gutter and etc.
Wooden: Wooden Furniture, Chipboard and etc.
APPLICATION INSTRUCTION







Clean the entire application surface.
Stir well before the application.
Dilute the KK233 by water with the recommended ratio depends on the purpose of use.
KK233 must be covered by cement screed or water-based paint to avoid it from exposed
to sun as it is not the finishing paint.
By spraying, rolling and brushing
Coverage approximately 5~10m2/L.
Do not apply when the weather is rainy, foggy or wet.
*Based on the actual circumstances of the site, the construction method is necessary to do adjustment
appropriately.
I
PRODUCT INTRODUCTION SHEET
KK233 ENHANCED INTERFACE EMULSION (PRIMER)
COLOUR
Colourless
TECHNICAL DATA
Test Items
Portable Adhesion Test
(kgf/cm2)
Tensile Strength (kgf/cm2)
Elongation (%)
Tear Strength (kgf/cm)
Acid Resistance
(5% H2SO4, 23ºC, 96 hrs)
a. Tensile Strength (kgf/cm2)
b. Elongation (%)
Alkali Resistance
(5% NaOH, 23ºC, 96 hrs)
a. Tensile Strength (kgf/cm2)
b. Elongation (%)
Deterioration in an Air Oven
(100ºC, 70 hrs)
a. Tensile Strength (kgf/cm2)
b. Elongation (%)
Adhesion
Salt-Water Resistance
(5% NaCl, 23ºC, 24 hrs)
Water Vapor Transmission of
Materials (g/24h•m2)
UV Test
a. Tensile Strength (kgf/cm2)
b. Elongation (%)
Coefficient of friction
(Dry fiction)
Tests Methods
Refer to ASTM D4541-09el
ASTM D412-06ae2
(Die C,V=500mm/min)
ASTM D624-00(2007)
(Die C,V=500mm/min)
ASTM D543-06 &
ASTM D412-06ae2
(Die C,V=500mm/min)
Test Results
19.1
(Tile destruction)
39.1
318
30.8
55.1
277
54.3
290
ASTM D573-04(2010) &
ASTM D412-06ae2
(Die C,V=500mm/min)
106
3.54
ASTM D3359-09
Method B
5B (Remark 1)
ASTM D1308-02(2007)
(Immerse)
No abnormality even
immersed in sodium chloride
solution.
ASTM E96-05
Procedure B
ASTM G155-05a cycle 1 &
ASTM D412-06ae2
(Die C, V=500mm/min)
Refer ASTM D1894-08
C-Type
(Sled Plane: rubber,
mass of weight and
specimen: 217.7g)
2.41
54.7
265
0.48
*Based on the actual circumstances of the site, the construction method is necessary to do adjustment
appropriately.
II
PRODUCT INTRODUCTION SHEET
KK233 ENHANCED INTERFACE EMULSION (PRIMER)
SAFETY & HEALTH


Rinse with plenty of water and consult doctor immediately if the coating splash into eyes.
Wash with water if the coating contacted to skin. (No need thinner)
PACKAGING




Pail/300 ML ± 5%
Pail/2 Litre ± 5%
Pail/5 Litre ± 5%
Pail/20 Litre ± 5%
SHELF LIFE


3 years in an unopened container and stored in a cool and dry place.
Reseal the remaining coating properly and keep it in store.
*Based on the actual circumstances of the site, the construction method is necessary to do adjustment