PU 240-10
gb 11/0117
2K PU Top Coat matt
page 1 / 2
Product Information
Product description
Operational Sector :
2K-polyurethane-acryl high performance coating suitable for
commercial vehicles, facade construction elements and heavily strained
machines and constructions.
Specification :
Binder base:
Solid content:
Delivery viscosity (DIN 53 211):
Density (DIN EN ISO 2811):
Gloss (DIN EN ISO 2813):
Polyurethane-acryl-system
57 - 63 by weight -%
42 - 43 by volume -%
140 - 160 s 4 mm DIN
1.20 - 1.40 kg / l
10 - 20 units / 60° (matt)
Features :
-
electrostatically applicable
high UV- and weathering resistance
excellent water resistance
resistance to solvents
scratch proof
short-term temperature exposure: 180°C
permanent temperature exposure: 150°C
Theoret. Consumption :
25.3 - 29.4 m / kg (by 10 µm dry coat thickness)
2
29.6 - 31.6 m / l (by 10 µm dry coat thickness)
Storage :
In tightly closed original containers at least 3 years shelf life
2
Application
Processing Conditions:
From + 10 °C and up to 80 % relative air humidity.
Substrate Preparation :
Steel: clean, eventually sand (remove rust, cinder, oxides) and
degrease with Mipa Silikonentferner (anti - silicone).
Zinc: clean with ammonia alkaline wetting agent.
Aluminium: clean, sand and degrease with Mipa Silikonentferner (antisilicone).
Application Process :
Pressure [bar]
Nozzle [mm]
3-5
2.5 - 3
120 - 150
1.3 - 1.5
1.3 - 1.4
0.28 - 0.33
(65 - 95 °)
Air / Flow jar
HVLP
Airless
Spraying
Operations
2-4
2-4
1
Dilution :
Mipa 2K-Verdünnung
Hardener :
Mipa 2K-Härter H 5, H 10, H 25
Mipa 2K-MS-Härter MS 10, MS 25, MS 40
Mipa 2K-PU-Härter PU 914-10, PU 914-25, PU 914-40
Mipa 2K-PU-Härter PU 916-10, PU 916-25
Mipa 2K-PU-Härter PU 933-05, PU 933-10
Mipa PUR Plus-Härter A 60 (application by brush or roller)
Thinner
10 - 15 %
10 - 15 %
unthinned
This technical data sheet is supplied for informational purposes only! According to our information, all data and recommendations correspond to the
state of art and are based on years of experience in manufacturing our products. They do not exempt the user from his obligation to verify professionally,
on his own responsibility, the suitability of our products to the intended purpose under prevailing conditions. Safety data sheets and warnings on
packaging must be observed. We reserve the right to modify and to complete the information content at any time, without prior notice or obligation to
update.
MIPA SE · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100
PU 240-10
gb 11/0117
2K PU Top Coat matt
page 2 / 2
Product Information
Mixing Ratio :
With 2K-Härter H 5, H 10, H 25, MS 10 / 2K-MS-Härter MS 10, MS 25,
MS 40 / 2K-PU-Härter PU 933-05, PU 933-10
by weight:
3 : 1 (paint : hardener)
by volume: 2 : 1 (paint : hardener)
With 2K-PU-Härter PU 914-10, PU 914-25, PU 914-40
by weight:
4 : 1 (paint : hardener)
by volume: 3 : 1 (paint : hardener)
With 2K-PU-Härter PU 916-10, PU 916-25, PUR Plus-Härter A 60:
by weight:
5 : 1 (tinter : hardener)
by volume: 4 : 1 (tinter : hardener)
Dry
Object temp. 20 °C
Object temp. 60 °C
dust dry
25 - 30 min.
set to touch
2-3h
handle
6-8 h
30 min.
recoatable
-
Full cure after 5 - 6 days (20 °C).
Pot Life :
1 - 8 hours
Application Proposal :
Steel:
Base coat:
Top coat:
EP 100-20 (coat thickness: 50 - 70 µm)
PU 240-10 (coat thickness: 50 - 60 µm)
Zinc:
Base coat:
Top coat:
EP 100-20 (coat thickness: 50 - 70 µm)
PU 240-10 (coat thickness: 50 - 60 µm)
Aluminium:
Base coat:
EP 100-20 (coat thickness: 25 - 30 µm)
Top coat:
PU 240-10 (coat thickness: 50 - 60 µm)
Special remarks
To be used only by professionals. Unique UV-resistant pigmentations (for example for facade coating)
are available on request.
Besides there is the possibility to mix fluorescent paints Mipa Neon-Farbtöne which are designated for
one coat application. In this case please see the Product Information “Mipa Neon-Farbtöne PMIEinschichtlacke”. Please check for colour accuracy prior to use.
In a paint system with EP 100-20, this product (in all lead- and chromate-free colours) can be applied
safely on machines which are used to process dry food (e.g. corn) and may come thereby in direct
contact with foodstuff. The abrasion behaviour is part of the approval (ISEGA certificate 43517 U 16 +
supplement approving the compliance with the specification of Regulation ((EC)) No 1935/2004 Article 3
and examination of abrasion behaviour according to FDA §177.1680).
Cleaning of Tools
Tools should be cleaned immediately after use with cellulosic thinner Mipa Nitroverdünnung.
This technical data sheet is supplied for informational purposes only! According to our information, all data and recommendations correspond to the
state of art and are based on years of experience in manufacturing our products. They do not exempt the user from his obligation to verify professionally,
on his own responsibility, the suitability of our products to the intended purpose under prevailing conditions. Safety data sheets and warnings on
packaging must be observed. We reserve the right to modify and to complete the information content at any time, without prior notice or obligation to
update.
MIPA SE · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100