CONTROLLED COPY BEPL/ML/PS/52A PRODUCT SPECIFICATION GRADE FEATURE PRESENTATION ABSTRON; MIF-45 EP GOOD IMPACT,HIGH FLOW ,ELECTROPLATING GRADE NATURAL TYPICAL PROPERTY DATA PROPERTIES ASTM TEST TEST CONDITION METHOD UNIT Page No:01 of 01 Issue No: 02 Issue Date: 19/08/09 INJECTION TOLERANCE Revision No: 01 MOULDED Revision Date: 19/08/09 VALUE PHYSICAL PROPERTIES at 23 deg C Melt Flow Rate D-1238 Specific Gravity* D-792 Mould Shrinkage* D-955 220°C/10kg gm/10 min 43 +/- 3 - 1.045 +/- 0.005 % 0.5 +/- 0.1 THERMAL PROPERTIES Heat Deflection Temeprature* 12.7mm x 6.4mm x 127mm Bar D-648 18.56 Kg/cm² Annealed at 85 Deg C/2 Hr °C 93 +/- 2 Vicat Softening Temeprature* D-1525 Rate-B,50N °C 97 +/- 3 Flammability Rating at 0.32 cm* UL-94 - HB - Coefficient of linear Thermal expansion* D-696 (23-55°C) 10E-4/ C 0.8 +/- 0.2 Notched Izod Impact Strength D-256 D-256 6.4 mm 3.2 mm Kgf cm/cm Kgf cm/cm 22 28 +/- 2 +/- 2 Tensile Strength at yield D-638 5 mm/min Kg/cm² 420 +/- 20 Tensile Strength at yield * D-638 50 mm/min Kg/cm² 460 +/- 20 Tensile Modulus* D-638 50 mm/min Kg/cm² 24000 +/- 1000 Yield Flexural Strength* D-790 5 mm/min Kg/cm² 650 +/- 30 Flexural Modulus* D-790 5 mm/min Kg/cm² 22500 +/- 1000 Hardness, Rockwell R D-785 R-scale 110 +/- 2 0 MECHANICAL PROPERTIES * To be measured as and when necessary * It is necessary to pre-dry material at 85~900C for 2 to 3 hours prior to processing. * Injection molding conditions- 190 - 230oC * Disclaimer - The values have been determined on standard Test specimens made using injection moulding.We do not stand warranty of any type that these values are reproducible as the physical and other properties will vary subject to moulding conditions, test specimen preparation etc.
© Copyright 2024 Paperzz