BAHAN BANGUNAN ALAMI - METAL
week 10
METAL
BAHAN METAL (LOGAM) BERASAL DARI BAHASA YUNANI METALLON,
YANG ARTINYA UNSUR KIMIA YANG SIAP MEMBENTUK ION DAN
MEMBENTUK IKATAN LOGAM
SIFAT DASAR DARI METAL ADALAH :
1.
2.
3.
4.
5.
TIDAK TEMBUS CAHAYA
MENGKILAP BILA DIGOSOK
KONDUKTOR PANAS DAN LISTRIK YANG BAIK
BISA DIBENTUK (UMUMNYA DITEMPA)
MEMPUNYAI TITIK LEBUR YANG TINGGI
FERROUS METAL
• LOGAM YANG MENGANDUNG BESI
• TIPE LOGAM YANG PALING UMUM DI LAS
• MENGANDUNG MAGNET
• BERSIFAT KARAT , CIRI-CIRINYA :
 BERCAK KEHIJAUAN
 WARNA LOGAM JADI KUSAM
BEBERAPA JENIS FERROUS METAL :
1. BESI TUANG ( CAST IRON )
2. BESI TEMPA ( WROUGHT IRON )
3. BESI ALLOY
PADA PRINSIPNYA KE-3 JENIS FERROUS METAL
TERBUAT DARI BIJIH BESI YANG DICAIRKAN
DAN DIPRES ULANG MENJADI BENTUK
BARU.
KOROSI
KOROSI ADALAH :
PROSES TERJADINYA KARAT BERUPA RUSAKNYA LOGAM
YANG BEREAKSI KIMIA DENGAN LINGKUNGAN DIMANA
LOGAM BEREAKSI MENJADI ION PADA PERMUKAAN
LOGAM YANG BERHUBUNGAN LANGSUNG DENGAN
LINGKUNGAN BERAIR DAN OKSIGEN.
KOROSI
FAKTOR YANG MEMPENGARUHI KOROSI ADALAH :
1. KELEMBABAN UDARA
2. LAPISAN PADA PERMUKAAN LOGAM
3. ADANYA O2
HAL YANG DILAKUKAN UNTUK MENCEGAH KOROSI ADALAH :
1. DI CAT
2. DILAPISI LOGAM YANG LEBIH MULIA
3. DICAMPUR DENGAN LOGAM LAIN
BESI GALVANIS :
BESI YANG SUDAH MELALUI PROSES KIMIA UNTUK
MENGHINDARI KOROSI, BERUPA PELAPISAN DENGAN
ZINC AGAR BESI TAHAN KARAT
BESI
UNSUR BESI (FE) MERUPAKAN ELEMEN PENYUSUN
UTAMA DARI LOGAM, BERSIFAT LUNAK DAN
BERWARNA KEKUNING-KUNINGAN.
JARANG DITEMUKAN DALAM BENTUK NON ALLOY
KECUALI DI LABORATORIUM UNTUK KEPERLUAN
KHUSUS.
PADA DASARNYA BESI SANGAT MUDAH MELEPASKAN
UNSUR KARBON DAN SLAG (KERAK), SEHINGGA MUDAH
UNTUK DIPROSES DENGAN UNSUR LAINNYA, SEPERTI
CR, SI, MN DLL
BESI YANG MENGANDUNG BANYAK CARBON AKAN
MEMBUAT SIFAT BESI MENJADI KERAS DAN KUAT
TAPI JUGA GETAS ( MUDAH PATAH)
SUNGAI MERAH MENGANDUNG BIJIH BESI
BESI
BEBERAPA CONTOH PERLAKUAN PADA BESI
BESI TUANG (CAST IRON)
• TERBUAT DARI BIJIH BESI YANG DILELEHKAN DI TUNGKU PEMBAKARAN
DAN DI TUANG KE DALAM CETAKAN.
• WARNANYA ABU-ABU GELAP
• MEMPUNYAI SIFAT YANG KERAS NAMUN MUDAH PATAH
BESI TEMPA (WROUGH IRON)
• PEMBENTUKAN BESI DENGAN DITEMPA MENJADI SERAT YANG
PANJANG, SIFAT STRUKTURNYA MUDAH DITEMPA, DAN LEBIH
KUAT DARI PADA BESI TUANG .
• WARNA ABU-ABU TERANG
• JENIS BESI TEMPA :
BAR IRON ( PLAT)
ROD IRON ( PIPA )
PLATE IRON ( LEMBARAN )
DETAIL SAMBUNGAN WROUGHT IRON
BESI ALLOY
BESI ALLOY MERUPAKAN BESI YANG DIBENTUK DARI PERPADUAN 2 ATAU LEBIH
UNSUR.
BEBERAPA CONTOH JENIS ALLOY ADALAH :
- IRON + CARBON
 STEEL ( BAJA )
- COPPER + ZINC
 BRASS ( KUNINGAN )
- ALUMINIUM + COPPER
 DURALUMIN
BAJA
BAJA ADALAH BENTUK LAIN BESI YANG HANYA
MENGANDUNG 2% CARBON
UNTUK MENINGKATKAN PEMANFAATAN BESI MAKA BAJA
DICAMPUR DENGAN MATERIAL LAIN, YAITU DIANTARANYA :
AL, MN, SI, S, P, CP, CR, N
PRODUK BESI ALLOYSTAINLESS STEEL
- MENGANDUNG 11% CHROME
- TIDAK MUDAH BERKARAT
- UMUM DIPAKAI DALAM INDUSTRI CUTLERY
DAN JAM TANGAN
ART DECO SCULPTURE, NEW YORK
UNFINISHED STAINLES STEEL
CROCKERY
CHRYSTLER BUILDING, NEW YORK
Beberapa jenis tampilan stainless steel :
BEBERAPA JENIS TAMPILAN STAINLESS STEEL
HAIRLINE FINISHED
MIRROR FINISHED
EMBOSSED FINISHED
TITANIUM COATED
ART FINISHED DECORATIVE
CD PATTERN FINISHED
ATAP BAJA RINGAN
MEMPUNYAI KELEBIHAN :
* SUDAH MELALUI PROSES GALAVANIS
* KUAT DAN TAHAN LAMA
* ANTI RAYAP
* TAHAN KARAT
* TAHAN CUACA
* STRUKTUR LEBIH RINGAN
* PEMASANGAN LEBIH CEPAT
* TIDAK BERSIFAT MEMBESARKAN API
* MENGURANGI PENGGUNAAN KAYU
MEMPUNYAI KEKURANGAN :
* TIDAK BISA DIEKSPOS KARENA RANGKANYA
TIDAK MENARIK UNTUK DIEKSPOS
* TIDAK FLEKSIBEL SEPERTI KAYU YANG BISA
DIPOTOND DAN DIBENTUK PROFIL
KONSTRUKSI & FURNITURE
HOUSEHOLD
PENAMBAHAN SIFAT DARI LOGAM
1.
2.
3.
4.
5.
6.
7.
8.
PENURUNAN CARBON < 0.9 %
MENINGKATKAN KEKUATAN DAN KEKAKUAN.
PENAMBAHAN MANGAN 0.5 – 2%
MENINGKATKAN KEKUATAN DAN KEKAKUAN.
PENAMBAHAN SILIKON KURANG DAR 2.5%
MENINGKATKAN KEKUATAN DAN KEKAKUAN.
PENAMBAHAN SULFUR KURANG DR 0.05%
MENINGKATKAN TITIK LELEH 0.05 – 3% MENINGKATKAN PENGERJAAN
DENGAN MESIN
PENAMBAHAN FOSFOR <0.05%
MENINGKATKAN KEKUATAN DAN DAYA TAHAN TERHADAP KARAT
PENAMBAHAN TEMBAGA <0.25%
MENINGKATKAN KEKUATAN DAN DAYA TAHAN TERHADAP KARAT
PENAMBAHAN CHROME 4 – 12%
MENINGKATKAN KEKUATAN PADA SUHU TINGGI DAN KETAHANAN
TERHADAP KOROSI
PENAMBAHAN NIKEL 1 – 4%
MENINGKATKAN KEKUATAN DAN KEKAKUAN